1-component mounting and filling foam for single application Chemical basis: Moisture curing polyurethane prepolymer Colour: Champagne coloured Density: 25 kg/m³ Density conditions: in accordance with DIN EN ISO 845 Smell/fragrance: Characteristic Moulded density: 25 kg/m³ Tack-free after: 10 min Conditions for being tack-free: at 20°C and 65% humidity with 30-mm adhesive line Can be cut after: 3 h Conditions for ability to cut: at 20°C and 65% relative humidity at 30-mm adhesive line Full resilience: 24 h Min. processing temperature: 5 °C Max. processing temperature: 30 °C Min. ambient processing temperature: 0.01 °C Min. surface processing temperature: 5 °C Max. processing temperature for can: 0.01 °C Min./max. temperature resistance: -40 to 90 °C Max. short-term temperature resistance: 120 °C Heat conductance λ: 0.01 W/(m*K) Heat conductance λ conditions: in accordance with DIN 52612 Flexural strength: 0.01 N/mm² Conditions for flexural strength: in accordance with DIN 53423 Shear strength: 0.01 N/mm² Conditions for shear strength: in accordance with DIN 53427 Compressive strength: 0.01 N/m Compressive strength conditions: in accordance with DIN 53421 Breaking elongation: 10 % Breaking elongation conditions: in accordance with DIN 53571 Yield (volume) approx.: 19 l Conditions for yield: Foam yield (free foaming) Contents: 750 ml Container: Can Weight of content: 10 g Building material class: B3 – Of high flammability Building material class conditions: in accordance with DIN 4102 Shelf life from production: 12 Month Conditions to maintain shelf life from production: at 20°C Tack-free after: 10 min Conditions for being tack-free: at 20°C and 65% humidity with 30-mm adhesive line Can be cut after: 40 min Conditions for ability to cut: at 20°C and 65% relative humidity at 30-mm adhesive line Final spreading possible after: 2 h Conditions for final spreading: at 20°C and 65% relative humidity at 30-mm adhesive line Full resilience: 12 h Conditions for full resilience: at 20°C and 50% relative humidity Min. processing temperature: 5 °C Max. processing temperature: 30 °C Min. surface processing temperature: 5 °C Max. surface processing temperature: 35 °C Min. temperature resistance: -40 °C Max. temperature resistance: 90 °C Building material class: B3 – Of high flammability Building material class conditions: in accordance with DIN 4102 Heat conductance λ: 0.032 W/(m*K) Heat conductance λ conditions: in accordance with DIN 52612 Compression strength: 0.3 N/mm² Compression strength conditions: in accordance with DIN 53421 Conditions for acoustic insulation of joints: in accordance with DIN 52210 Acoustic insulation for 10 mm-wide joint: -1 dB Acoustic insulation for 20 mm-wide joint: -6 dB Ultraviolet resistance: No Breaking elongation: 25 % Breaking elongation conditions: in accordance with DIN 53571 Flexural strength: 0.7 N/mm² Conditions for flexural strength: in accordance with DIN 53423 Shear strength: 0.17 N/mm² Conditions for shear strength: in accordance with DIN 53427 Yield (volume) approx.: 40 l Conditions for yield: Foam yield (free foaming) Contents: 750 ml Container: Can Weight of content: 735 g Shelf life from production: 12 Month Conditions to maintain shelf life from production: at 20°C